www.bond-laminates.de

	TEPEX® dynalite
	· Glass/PP
	· Glass/TPU, Carbon/TPU
	· Glass/PA6, Carbon/PA6 Glass/PA66, Carbon/PA66 Glass/PA12, Carbon/PA12
	· Glass/PPS, Carbon/PPS

	TEPEX® flowcore
	· Glass/PA6

	TEPEX® anti-ballistic
	· Aramid/PA

Newsworthy

Conferences

TEPEX® dynalite material solutions based on TPU

TEPEX® xx8: thermoplastic polyurethane is transparent, which allows the use of decorative weavings. The forming temperature is approx.210°C-230°C. The material can easily be formed, producing an outstanding finish. Forming into simple curves is even possible from 100°C. This material is consequently ideal for orthopaedics. In the sport industry, this material is ofteninsert-moulded with standard TPUs. The material is moreover easy to bond. Chemical resistance as PA12. The material exhibits outstanding properties at temperatures < 0°C. TEPEX® materials on a TPU basis exhibit the best mechanicalproperties.

TEPEX® dynalite 108 – Glass/TPU
TEPEX® Product	Specific weight Style - warp:weft	Thickness per layer	Product features	PDF	Picture
TEPEX® dynalite108-FGAL200(x)/45 %Filament Glass/TPU	200 g/m²Twill 50:50, silver	0.17 mm	Light aluminised woven fabric, finer structure thanFGAL290.
TEPEX® dynalite108-FG290(x)/45 % Filament Glass/TPU	290 g/m²Twill 50:50	0.25 mm	Can be formed at relatively low temperature.
TEPEX® dynalite108-FGAL290(x)/45 %Filament Glass/TPU	290 g/m² Silver, anthracite	0.25 mm	Attractive aluminium finish, available in two colours.
TEPEX® dynalite108-RGUD600(x)/45%Roving Glass/TPU	600 g/m² Plain -80:20	0.50 mm	Uni-directional 80:20 reinforcement suitable forstructural components. Ideal reinforcing material forthe ski industry.
TEPEX® dynalite108-RG600(x)/45 %Roving Glass/TPU	600 g/m² Twill 50:50	0.50 mm	Balanced 50:50 reinforcement suitable for structuralcomponents.

TEPEX® dynalite 208 – Carbon/TPU
TEPEX® Product	Specific weight Style - warp:weft	Thickness per layer	Product features	PDF	Picture
TEPEX® dynalite208-C160(x)/45 % Carbon/TPU	160 g/m² Plain 50:50	0.20 mm	Lightest 3k woven fabric solution. Somewhat moreopen woven structure.
TEPEX® dynalite 208-C190(x)/45 %Carbon/TPU	190 g/m² Plain -50:50	0.25 mm	Lightest 12k woven fabric solution. The fibre isstretched in this woven fabric. Dense structure.
TEPEX® dynalite208-C200(x)/45 % Carbon/TPU	200 g/m² Plain 50:50	0.25 mm	Our standard solution in 3k. The twill bindingassures ease of forming.