www.bond-laminates.de

	TEPEX® dynalite
	· Glass/PP
	· Glass/TPU, Carbon/TPU
	· Glass/PA6, Carbon/PA6 Glass/PA66, Carbon/PA66 Glass/PA12, Carbon/PA12
	· Glass/PPS, Carbon/PPS

	TEPEX® flowcore
	· Glass/PA6

	TEPEX® anti-ballistic
	· Aramid/PA

Newsworthy

Conferences

TEPEX® dynalite material solutions based on PA66

TEPEX® xx2: polyamide 6 with a very good price/performance ratio and is available in transparent and black. The forming temperature is approx. 240°C-260°C. Applications are mainly found in the sport industry, automotive industry and miscellaneous industrial products. Continuous operating temperature is 120°C. Polyamide 6 has a good chemical resistance against oils and light acids. The material is often applied in the automotive industry.

TEPEX® dynalite 102 – Glass/PA6
TEPEX® Product	Specific weight Style - warp:weft	Thickness per layer	Product features	Picture
TEPEX® dynalite 102-FGAL200(x)/45 % Filament Glass/PA6	200 gr/m² Twill - 50:50, silver	0.17 mm	Light aluminised fabric, finer structure than FGAL290.
TEPEX® dynalite 102-FG290(x)/45 % Filament Glass/PA6	290 gr/m² Twill - 50:50	0.25 mm	Light, chemical resistant, good mechanical properties, continuous operating temperature 120°C.
TEPEX® dynalite 102-FGAL290(x)/45 % Filament Glass/PA6	290 gr/m² silver, blue, anthracite	0.25 mm	Attractive aluminium surface, available in 3 colours.
TEPEX® dynalite 102-RGUD600(x)/45 % Roving Glass/PA6	600 gr/m² Plain - 80:20	0.50 mm	Uni-directional 80:20 reinforcement suited for structural parts. Ideal automotive material.
TEPEX® dynalite 102-RG600(x)/45 % Roving Glass/PA6	600 gr/m² Twill - 50:50	0.50 mm	Balanced 50:50 reinforcement suited for structural parts. Ideal automotive material.

TEPEX® dynalite 502 – Aramid/Carbon/PA6 – natural
TEPEX® Product	Specific weight Style - warp:weft	Thickness per layer	Product features	Picture
TEPEX® dynalite 502-CA210(x)/45 % Carbon/Aramid/PA6	210 gr/m² Twill – 50:50	0.20 mm	Hybrid fabric of 3k carbon and aramid fibres.

TEPEX® dynalite material solutions based on PA66

TEPEX® xx1: polyamide 66 with very good price/performance ratio. Available in transparent and black. The forming temperature is approx. 280°C-300°C. Applications are mainly found in the sport industry, automotive industry and miscellaneous industrial products. The continuous operating temperature is at 130°C slightly higher than for PA6. Polyamide 6 has a good chemical resistance against oils and light acids.

TEPEX® dynalite 101 – Glass/PA66
TEPEX® Product	Specific weight Style - warp:weft	Thickness per layer	Product features	Picture
TEPEX® dynalite 101-FG290(x)/45 % Filament Glass/PA66	290 gr/m² Twill - 50:50	0.25 mm	Light, chemical resistant, good mechanical properties, continuous operating temperature 130°C.
TEPEX® dynalite 101-RGUD600(x)/45 % Roving Glass/PA66	600 gr/m² Plain - 80:20	0.50 mm	Uni-directional 80:20 reinforcement suited for structural parts. Ideal automotive material, in case a higher temperature resistance than that of PA6 is needed.
TEPEX® dynalite 101-RG600(x)/45 % Roving Glass/PA66	600 gr/m² Twill - 50:50	0.50 mm	Balanced 50:50 reinforcement suited for structural parts. Ideal automotive material.

TEPEX® dynalite 201 – Carbon/PA66
TEPEX® Product	Specific weight Style - warp:weft	Thickness per layer	Product features	Picture
TEPEX® dynalite 201-C160(x)/45 % Carbon/PA66	160 gr/m² Plain - 50:50	0.20 mm	Lightest 3k fabric solution. Slightly Open fabric structure.
TEPEX® dynalite 201-C190(x)/45 % Carbon/PA66	190 gr/m² Plain – 50:50	0.25 mm	Lightest 12K fabric solution. In this fabric, the fibre has been spread. Dense structure.
TEPEX® dynalite 201-C200(x)/45 % Carbon/PA66	200 gr/m² Twill – 50:50	0.25 mm	Our standard solution with 3k fibres. The Twill fabric style ensures good formability.

TEPEX® dynalite 501 – Aramid/Carbon/PA6 - natural
TEPEX® Product	Specific weight Style - warp:weft	Thickness per layer	Product features	Picture
TEPEX® dynalite 501-CA210(x)/45 % Carbon/Aramid/PA66	210 gr/m² Twill – 50:50	0.20 mm	Hybrid fabric of 3k carbon and aramid fibres.

TEPEX® dynalite material solutions based on PA12

TEPEX® xx6: polyamide 12. Available in transparent and black. Forming temperature approx. 190°C-220°C. Applications in the sport industry as well as industrial products. Continuous use temperature around 90°C. PA12 is especially suited if a good surface quality from the mould is needed. Therefore the material is used mostly in combination with carbon and aluminised fabrics.

TEPEX® dynalite 106 – Glass/PA12
TEPEX® Product	Specific weight Style - warp:weft	Thickness per layer	Product features	Picture
TEPEX® dynalite 106-FG50(x)/28 % Filament Glass/PA12	50 gr/m² Plain - 50:50	0.07 mm	Our lightest fabric gives a material thickness of only 50 µm and is often used as facing layer for sandwich materials.
TEPEX® dynalite 106-FGAL200(x)/45 % Filament Glass/PA12	200 gr/m² Twill - 50:50, silver	0.17 mm	Light aluminised fabric, finer structure than FGAL290.
TEPEX® dynalite 106-FG290(x)/45 % Filament Glass/PA12	290 gr/m² Twill - 50:50	0.25 mm	Can be formed at relatively low Temperatures.
TEPEX® dynalite 106-FGAL290(x)/45 % Filament Glass/PA12	290 gr/m² silver, blue, anthracite	0.25 mm	Attractive aluminium surface, available in two colours.

TEPEX® dynalite 206 – Carbon/PA12
TEPEX® Product	Specific weight Style - warp:weft	Thickness per layer	Product features	Picture
TEPEX® dynalite 206-C160(x)/45 % Carbon/PA12	160 gr/m² Plain - 50:50	0.20 mm	Lightest 3k fabric solution. Slightly Open fabric structure.
TEPEX® dynalite 206-C200(x)/45 % Carbon/PA12	200 gr/m² Twill – 50:50	0.25 mm	Our standard solution with 3k fibres. The Twill fabric style ensures good formability.